KANEVINYL T5DA
鋁箔熱封膠、金屬涂層
Technical Data Sheet
Kanevinyl T5DA
Item | Figures | Method |
Vinyl Chrolide content ( % ) | 81 | |
Vinyl Acetate content ( % ) | 18 | Kaneka Method |
Carboxyl monomer content ( % ) | 1 | |
Acid value ( mg?KOH/g ) | 8 | Kaneka Method |
K Value ( - ) | 51 | ISO 1269 ? JIS K7367-2 |
Polyme rization Degre e ( - ) | 480 | ISO 1269 ? JIS K7367-2 |
Tg ( glass transition temp. ℃ ) | 71 | DSC Method、JIS K7121 、ISO 3146 |
Solution viscosity | ||
Type B viscometer ( cps ) | 280 | measured at 25℃?Resin / EAC = 20/80 solution dissolved at 30℃ |
Type B viscometer ( cps ) | 950 | measured at 25℃?25% 、 MEK/TOL/BAC = 1/1/3 solution dissolved at 30℃ |
Above data and information are based on our reliable test.
This is only reference figures, not guaranteed ones