Technical Data Sheet
Kanevinyl T555
Item | Quantitative specs. Kanevinyl T555 | Method |
Clarity | clear | 20% solution in MIBK/Toluene=1/1 |
Vinyl Chrolide content ( % ) | 84 | |
Vinyl Acetate content ( % ) | 14 | Kaneka Method ( FT- IR ) |
Hydroxyl Group content ( % ) | 2 | Kaneka Method ( modified JIS K0070 ) Neutralization analysis by Acylation |
Acid Value ( mgKOH/g resin ) | 0.5 | Kaneka Method ( modified JIS K0070 ) Neutralization analysis |
K Value ( - ) | 46 | IS0 1269、 JIS K7367-2 |
Polymerization Degree ( - ) | 350 | IS0 1269、 JIS K7367-2 |
Molecular Weight ( - ) | 35000 | Kaneka Method |
Tg (glass transition temp. ℃) | 71 | DSC Method JIS K7121、ISO 3146 |
Particle size ( μm ) Distribution of praticle size more than 355 μm less than 75 μm | 170 <1 <5 | JIS Z8801 mesh、ISO 2591、ISO Z8815 |
Appearance density ( g/ml ) | 0.66 | ISO 60、JIS K-7365 |
Solution viscosity Type B viscometer ( cps ) | 130 | measured at 25℃、25% MEK solution dissoived at 50℃ |
Above data and information are based on our reliable test.
Due to possible variations of conditions,guarantees are expressed by only above rnethod.